Hard porcelain
TFL-1
Ceramic material ECOBODY TFL-1, technical requirements TU U 14.2-32359731-001:2006 is a powder-like product, designed for the production of porcelain artistic-domestic wares by means of slip casting into gypsum moulds.
The product has stable quality, rather high whiteness of fired crock, necessary strength in dry state, excellent rheological properties (high fluidity with small content of deflocculating agents, low thixotropy, fast thickness formation and drying in gypsum mould).
The material is ideal for fast firing.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 62 | 27 | 0,34 | 0,45 | 0,3 | 0,2 | 2,4 | 0,4 | 7,2 |
Ceramic-Physical properties
| Moisture content, %, not more | 6,0 |
| Mesh residue 63 µm, %, not more | 1,5 |
| Deflocculating agent demand, %, not more | 0,6 |
| MoR 110oC, MPa, not less | 2,5 |
| Total shrinkage, %, not more | 16,0 |
| Water absorption (1360oC), %, not more | 0,2 |
|
Colour after firing: L(светлота) *a (+red/-green) *b (+yellow/-blue) |
85,3 -0,3 +1,8 |
|
Recommended firing temperature, оС |
1320-1360 |
TFL-2
Ceramic material ECOBODY TFL-2, technical requirements TU U 14.2-32359731- 001:2006 is a powder-like product, designed for the production of porcelain artistic-domestic wares by means of slip casting into gypsum moulds.
The product has stable quality, rather high whiteness of fired crock, necessary strength in dry state, excellent rheological properties (high fluidity with small content of deflocculating agents, low thixotropy, fast thickness formation and drying in gypsum mould).
The material is ideal for fast firing.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 63,0 | 25,5 | 0,45 | 0,1 | 0,18 | 0,3 | 3,2 | 0,3 | 7,0 |
Ceramic-Physical properties
| Moisture content, %, not more | 6,0 |
| Mesh residue 63 μm, %, not more | 1,5 |
| Deflocculating agent demand, %, not more | 0,6 |
| MoR, MPa, not less | 2,5 |
| Total shrinkage, %, not more | 15,0 |
| Water absorption (1400оС), %, not more | 0,2 |
|
Colour after firing: L(lightness) *a (+red/-green) *b (+yellow/-blue) |
88,3 -1,1 +0,4 |
|
Recommended firing temperature, оС |
1340-1400 |
TFF-1
Ceramic material ECOBODY TFF-1, technical requirements TU U 14.2-32359731-001:2006 is the brick-formed or roll-formed plastic vacuum-processed body, designed for the production of porcelain wares by means of slip casting and plastic forming.
The product has stable quality, rather high whiteness after firing, good forming and molding properties, high strength in dry state.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 62,0 | 27,0 | 0,34 | 0,45 | 0,3 | 0,2 | 2,4 | 0,4 | 7,2 |
Ceramic-Physical properties
| Moisture content, %, not more | 24,0 |
| Mesh residue 63 µm, %, not more | 1,5 |
| Deflocculating agent demand, %, not more | 0,5 |
| MoR 110oC, MPa, not less | 2,5 |
| Total shrinkage, %, not more | 18,0 |
| Water absorption (1360oC), %, not more | 0,2 |
|
Colour after firing: L(lightness) *a (+red/-green) *b (+yellow/-blue) |
85,3 -0,3 +1,8 |
|
Recommended firing temperature, оС |
1320-1360 |
TF-1I
Ceramic material ECOBODY TF-1I, technical requirements TU U 14.2- 32359731-001:2006 is a powder-like product, designed for the production of porcelain artistic-domestic wares by means of isostatic pressing.
The product is perfectly pressed and has stable quality, rather high whiteness after firing, necessary strength in dry state, ideal characteristics for pressing.
The material is ideal for fast firing.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 62,0 | 27,0 | 0,34 | 0,45 | 0,3 | 0,2 | 2,4 | 0,4 | 7,2 |
Ceramic-Physical properties
| Moisture content, %, not more | 4,0 |
| Mesh residue 63 μm, %, not more | 1,5 |
| MoR, MPa, not less | 3,0 |
| Total shrinkage, %, not more | 12,0 |
| Water absorption (1360оС),%, not more | 0,2 |
|
Colour after firing: L(lightness) *a (+red/-green) *b (+yellow/-blue) |
85,3 -0,3 +1,8 |
|
Recommended firing temperature, оС |
1320-1360 |
TF-2I
Ceramic material ECOBODY TF-2I, technical requirements TU U 14.2-32359731- 001:2006 is a powder-like product, designed for the production of porcelain artistic-domestic wares by means of isostatic pressing.
The product has stable quality, rather high whiteness after firing, necessary strength in dry state, ideal characteristics for pressing.
The material is ideal for fast firing.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 63,0 | 25,0 | 0,45 | 0,1 | 0,18 | 0,3 | 3,3 | 0,3 | 7,4 |
Ceramic-Physical properties
| Moisture content, %, not more | 3,0 |
| Mesh residue 63 μm, %, not more | 1,5 |
| Total shrinkage, %, not more | 12,0 |
| Water absorption (1400оС), %, not more | 0,2 |
|
Colour after firing: L(lightness) *a (+red/-green) *b (+yellow/-blue) |
88,3 -1,1 +0,4 |
|
Recommended firing temperature, оС |
1340-1400 |
The technical data presented here are indicative only. All sales are undertaken in accordance with “Donbas Ceramic Bodies” LLC conditions of sales.
The present product is produced in the supervised conditions determined by the Management Quality System which function in accordance with ISO 9001:2015 demands and has BV Certification. Number of Certificate: UA229088