PFL-1

Ceramic material ECOBODY PFL-1, technical requirements TU U 14.2-32359731-001:2006 is a powder-like product, designed for the production of semi-porcelain wares by means of slip casting into gypsum moulds.

The product has stable quality, rather high strength in dry state, excellent rheological properties (high fluidity with small content of deflocculating agents, low thixotropy, fast thickness formation and drying in gypsum mould).

The material is ideal for fast firing both in gas and in electric kilns.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
68,7 20,8 0,5 0,6 0,4 0,25 2,45 0,5 6,3

Ceramic-Physical properties

Moisture content, %, not more
6,0
Mesh residue 63 µm, %, not more 3,50
Deflocculating agent demand, %, not more 0,40
MoR 110oC, MPa, not less 3,0
Total shrinkage, %, not more
13,0
Water absorption (1220oC), %, not more
6,50
Recommended firing temperature, оС
1180-1220

PFL-2

Ceramic material ECOBODY PFL-2, technical requirements TU U 14.2-32359731-001:2006 is a powder-like product, designed for the production of semi-porcelain wares with improved aesthetic and operating qualities by means of slip casting into gypsum moulds.

Product has stable quality, rather high strength in dry state, excellent rheological properties (high fluidity with small content of deflocculating agents, low thixotropy, fast thickness formation and drying in gypsum mould).

The material is ideal for fast firing both in gas and in electric kilns.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
67,7 21,4 0,45 0,5 0,35 0,2 1,9 0,65 6,9

Ceramic-Physical properties

Moisture content, %, not more
6,0
Mesh residue 63 µm, %, not more 2,0
Deflocculating agent demand, %, not more 0,35
MoR 110oC, MPa, not less 3,0
Total shrinkage, %, not more
13,0
Water absorption (1280oC), %, not more
3,0
Recommended firing temperature, оС
1240-1280

PFF-2

Ceramic material ECOBODY PFF-2, technical requirements TU U 14.2-32359731-001:2006 is the brick-formed or roll-formed plastic vacuum-processed body, designed for the production of semi-porcelain wares by means of plastic forming into gypsum or metal moulds.

The product has stable quality, rather high plasticity and high strength in dry state. Due to high strengthening characteristics of the material after drying it is possible to glaze semi-finished product by dry crock and apply single firing.

The composition of the body has rather high whiteness in the fired condition. The material can be fired both in gas and in electric kilns.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
68,6 21,2 0,43 0,52 0,35 0,15 1,4 0,4 6,8

Ceramic-Physical properties

Moisture content, %, not more 23,50
Mesh residue 63 µm, %, not more 2,50
MoR 110oC, MPa, not less 3,0
Total shrinkage, %, not more 17,0
Water absorption (1280oC), %, not more
3,50
Recommended firing temperature, оС
1240-1280

PFF-4

Ceramic material ECOBODY PFF-4, technical requirements TU U 14.2-32359731-001:2006 is the brick-formed or roll-formed plastic vacuum-processed body, designed for the production of semi-porcelain acid-proof wares (Rashig’s rings, acid-proof tubes and shaped pieces for them etc.) and for building and decorative ceramic (elements of the fronts, landscape goods etc.), by means of plastic forming.

The product has stable quality, rather high plasticity properties, the material is ideal for fast firing both in gas and in electric kilns.

Due to proper melting during the firing’s process, material has high strength and density, acid resistance.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
67,0 21,1 0,50 0,6 0,4 0,33 3,14 0,65 6,2

Ceramic-Physical properties

Moisture content, %, not more 22,0
Mesh residue 63 µm, %, not more 3,0
MoR 110oC, MPa, not less 3,0
Total shrinkage, %, not more 15,0
Water absorption (1260oC), %, not more
1,0
Recommended firing temperature, оС
1200-1260

PFF-6

Ceramic material ECOBODY PFF-6, technical requirements TU U 14.2-32359731-001:2006 is the brick-formed or roll-formed plastic vacuum-processed body, designed for the production of ceramic tiles and for building and decorative ceramic (elements of the fronts, landscape goods etc.), by means of plastic forming.

The product has stable quality, rather high plasticity properties, relatively low vitrification temperature. Due to proper melting during the firing’s process, material has high strength and density.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
70,6 17,8 0,57 0,65 0,65 0,5 1,1 3,85 3,8

Ceramic-Physical properties

Moisture content, %, not more 19,0
Mesh residue 63 μm, %, not more 5,0
MoR, MPa, not less 3,0
Total shrinkage, %, not more 12,0
Water absorption (1200oC), %, not more 0,50
Recommended firing, оС
1150-1200

The technical data presented here are indicative only. All sales are undertaken in accordance with “Donbas Ceramic Bodies” LLC conditions of sales.

The present product is produced in the supervised conditions determined by the Management Quality System which function in accordance with ISO 9001:2015 demands and has BV Certification. Number of Certificate: UA229088