majolica
MKL-1
Ceramic material ECOBODY MKL-1, technical requirements TU U 14.2-32359731-001:2006 is a powder-like product, designed for the production of light-firing earthenware by means of slip casting into gypsum moulds.
The product has stable quality, rather high strength in dry state, excellent rheological properties (high fluidity with small content of deflocculating agents, low thixotropy, fast thickness formation and drying in gypsum mould).
The material is ideal for fast firing both in gas and in electric kilns.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 67,0 | 18,0 | 0,65 | 0,55 | 1,9 | 0,95 | 3,0 | 1,7 | 6,0 |
Ceramic-Physical properties
|
Moisture content, %, not more |
6,0 |
| Mesh residue 63 µm, %, not more | 4,5 |
| Deflocculating agent demand, %, not more | 0,3 |
| MoR 110oC, MPa, not less | 3,0 |
|
Total shrinkage, %, not more |
6,0 |
|
Water absorption (1100oC), %, not more |
18 |
|
Recommended firing temperature, оС |
1070-1100 |
MKL-2
Ceramic material ECOBODY MKL-2, technical requirements TU U 14.2-32359731-001:2006 is a powder-like product, designed for the production of light-firing earthenware by means of slip casting into gypsum moulds.
The product has stable quality, rather high strength in dry state, excellent rheological properties (high fluidity with small content of deflocculating agents, low thixotropy, fast thickness formation and drying in gypsum mould).
The material is ideal for fast firing both in gas and in electric kilns.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 68,0 | 21,7 | 0,60 | 0,68 | 0,3 | 0,25 | 1,3 | 0,2 | 6,0 |
Ceramic-Physical properties
|
Moisture content, %, not more |
6,0 |
| Mesh residue 63 µm, %, not more | 6,0 |
| Deflocculating agent demand, %, not more | 0,2 |
| MoR 110oC, MPa, not less | 2,5 |
|
Total shrinkage, %, not more |
7,0 |
|
Water absorption (1180oC), %, not more |
18 |
|
Recommended firing temperature, оС |
1160-1250 |
МКЛ-4
Ceramic material ECOBODY MKL-4, technical requirements TU U 14.2-32359731- 001:2006 is a powder-like product, designed for the production of light-firing earthenware by means of slip casting into gypsum moulds.
The product has stable quality, rather high strength in dry state, excellent rheological properties (high fluidity with small content of deflocculating agents, low thixotropy, fast thickness formation and drying in gypsum mould).
The material is ideal for firing both in gas and in electric kilns.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 69,1 | 17,9 | 0,7 | 0,7 | 1,2 | 0,65 | 3,1 | 1,65 | 4,75 |
Ceramic-Physical properties
| Moisture content, %, not more | 6,0 |
| Mesh residue 63 μm, %, not more | 4,50 |
| Deflocculating agent demand, %, not more | 0,40 |
| MoR, MPa, not less | 3,0 |
|
Total shrinkage, %, not more |
8,0 |
|
Water absorption (1100оC), %, not more |
15,0 |
|
Recommended firing temperature, оС |
1030-1100 |
MKF-1
Ceramic material ECOBODY MKF-1, technical requirements TU U 14.2-32359731-001:2006 is the brick-formed or roll-formed plastic vacuum-processed body, designed for the production of faience wares by means of plastic forming.
The product has stable quality, rather high plasticity and high strength in dry state and good forming properties.
The material can be fired both in gas and in electric kilns.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 68,7 | 21,50 | 0,55 | 0,65 | 0,35 | 0,2 | 0,8 | 0,2 | 7,2 |
Ceramic-Physical properties
|
Moisture content, %, not more |
24,0 |
| Mesh residue 63 µm, %, not more | 2,50 |
| MoR 110oC, MPa, not less | 5,0 |
|
Total shrinkage, %, not more |
15,0 |
|
Water absorption (1250oC), %, not more |
10 |
|
Recommended firing temperature, оС |
1170-1250 |
MKF-2
Ceramic material MKF-2, technical requirements TU U 14.2-32359731-001:2006 is the brick-formed or roll-formed plastic vacuum-processed body, designed for the production of light-firing earthenware by means both of hand forming and of machine forming into gypsum or metal moulds.
The product has stable quality, rather high plasticity and high strength in dry state. Due to high strengthening characteristics of the material after drying it is possible to glaze semi-finished product by dry crock and apply single firing both in gas and in electric kilns.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 68,4 | 18,0 | 1,0 | 1,25 | 1,8 | 0,4 | 1,8 | 0,4 | 6,6 |
Ceramic-Physical properties
|
Moisture content, %, not more |
23,50 |
| Mesh residue 63 µm, %, not more | 8,0 |
| MoR 110oC, MPa, not less | 5,0 |
|
Total shrinkage, %, not more |
12,0 |
|
Water absorption (1080oC), %, not more |
12,0 |
|
Recommended firing temperature, оС |
1050-1080 |
MKF-3
Ceramic material ECOBODY MKF-3, technical requirements TU U 14.2-32359731- 001:2006 is the brick-formed plastic vacuum-processed body, designed for the production of lightfiring earthenware of decorative purposes both for interior and exterior decorations (facade and landscape ceramics).
The product has stable quality, high strength in dry state and good forming properties. Due to high strengthening characteristics of the material after drying it is possible to glaze semi-finished product by dry crock and apply single firing both in gas and in electric kilns.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 66,8 | 20,3 | 0,8 | 1,0 | 1,5 | 0,3 | 2,4 | 0,5 | 5,9 |
Ceramic-Physical properties
|
Moisture content, %, not more |
21,50 |
| Mesh residue 63 μm, %, not more | 15,0 |
| Possible dispersion of fireclay filler, mm |
0-0,5 0-1 |
| MoR, MPa, not less | 4,0 |
|
Total shrinkage, %, not more |
15,5 |
|
Water absorption (1200оС), %, not more |
1,0 |
|
Recommended firing temperature, оС |
1150-1200 |
| Colour after firing (1200оС, full vitrification) | whity- beige |
The technical data presented here are indicative only. All sales are undertaken in accordance with “Donbas Ceramic Bodies” LLC conditions of sales.
The present product is produced in the supervised conditions determined by the Management Quality System which function in accordance with ISO 9001:2015 demands and has BV Certification. Number of Certificate: UA229088