Building ceramics
KR-1
Масса керамическая ECOBODY КР-1 (БСТ-1), ТУ У 14.2-32359731-001:2006 is a press-powder of definite granulometric content, designed for the production of double firing ceramic tiles by means of semi-dry pressing.
The product has stable quality, rather high strength in dry state.
The material is ideal for fast firing.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 62,5 | 15,0 | 1,2 | 0,75 | 5,0 | 2,3 | 2,0 | 0,6 | 10,5 |
Ceramic-Physical properties
| Moisture content, %, not more | 6,0 |
| Mesh residue 63 μm, %, not more | 6,50 |
| Fired bending strength, MPa, not less | 18,0 |
| Coefficient of linear thermal expansion, K-1 | (64,0-64,5)*10-7 |
| Total shrinkage, %, not more | 1,90 |
| Water absorption (1120oС), %, not more | 17,0 |
| Recommended firing temperature, oС | 1100-1120 |
KR-1P
Ceramic material ECOBODY KR-1P, technical requirements TU U 14.2-32359731-001:2006 is the brick-formed or the cake-formed plastic body (vacuum-processed brick-formed body or not vacuum-processed, friable).
The ceramic body is intended for the manufacture of light-burning porous ceramics for artistic and decorative purposes, products for building ceramics (mosaics, friezes, tiles for facing walls and fireplaces, etc.) by plastic molding.
The product has stable quality, good forming properties, high plasticity and durability in dry condition. Suitable for firing in both gas and electric kilns.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 62,5 | 15,0 | 1,2 | 0,75 | 5,0 | 2,3 | 2,0 | 0,6 | 10,5 |
Ceramic-Physical properties
| Moisture content, %, not more | 22,5 |
| Mesh residue 63 μm, %, not more | 6,5 |
| Strength limit in dry condition, MPa, not less | 3,0 |
| Flexural strength of fired sample, MPa, not less | 18,0 |
| Total shrinkage, %, not more | 10 |
| Water absorption (1050oС),%, not more | 16,0 |
| Recommended firing temperature, oС | 1050-1100 |
KR-2
Ceramic material ECOBODY KR-2, technical requirements TU U 14.2-32359731-001:2006 is a press-powder of definite granulometric content, designed for the production of vitrified tiles (technical porcelain) by means of semi-dry pressing.
Product has stable quality, rather high strength in dry state.
The material is ideal for fast firing.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 69,7 | 18,9 | 0,55 | 0,65 | 0,45 | 0,3 | 2,76 | 2,55 | 4,2 |
Ceramic-Physical properties
| Moisture content, %, not more | 6,0 |
| Mesh residue 63 µm, %, not more | 2,5 |
| Fired bending strength, MPa, not less | 50,0 |
| Total shrinkage, %, not more | 8,5 |
| Water absorption (1210oC), %, not more | 0,5 |
| Recommended firing temperature, oС | 1180-1210 |
КR-3
Ceramic material ECOBODY KR-3, technical requirements TU U 14.2-32359731-001:2006 is a press-powder of definite granulometric content, designed for the production of floor tiles, building ceramics (facade elements) by means of semi-dry pressing.
Product has stable quality, rather high strength in dry state.
The material can be fired both in gas and in electric kilns.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 69,2 | 19,5 | 1,0 | 1,0 | 0,3 | 0,35 | 3,3 | 0,6 | 5,3 |
Ceramic-Physical properties
| Moisture content, %, not more | 6,0 |
| Mesh residue 63 μm, %, not more | 4,0 |
| Fired bending strength, MPa, not less | 40,0 |
| Total shrinkage, %, not more | 8,50 |
| Water absorption (1160oС),%, not more | 3,5 |
| Recommended firing temperature, oС | 1130-1160 |
The technical data presented here are indicative only and used to familiarize Customers with the basic properties of the product. – 01/12/2019
The present product is produced in the supervised conditions determined by the Management Quality System which function in accordance with ISO 9001:2015 demands and has BV Certification. Number of Certificate: UA229088