Electro-technical wares
FET-1
Ceramic material ECOBODY FET-2, technical requirements TU U 14.2-32359731- 001:2006 is a powder-like product, designed for the production of electro-technical wares 111 sub-group (pressed silicate porcelain) by means of semi-dry pressing.
The product has stable quality, rather high strength in dry and fired state.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 67,7 | 20,9 | 0,57 | 0,66 | 0,35 | 0,25 | 3,05 | 0,75 | 5,8 |
Ceramic-Physical properties
|
Moisture content, %, not more |
6,0 |
| Mesh residue 63 μm, %, not more | 3,0 |
| MoR, MPa, not less | 50,0 |
|
Total shrinkage, %, not more |
14,0 |
|
Water absorption (1290оС),%, not more |
0,50 |
|
Recommended firing temperature, оС |
1260-1290 |
FET-2
Ceramic material ECOBODY FET-2, technical requirements TU U 14.2-32359731- 001:2006 is a powder-like product, designed for the production of electro-technical wares 111 sub-group (pressed silicate porcelain) by means of semi-dry pressing.
The product has stable quality, rather high strength in dry and fired state.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 67,0 | 21,7 | 0,55 | 0,55 | 0,4 | 0,22 | 2,5 | 0,9 | 5,7 |
Ceramic-Physical properties
|
Moisture content, %, not more |
6,0 |
| Mesh residue 63 μm, %, not more | 3,0 |
| Fired bending strength, MPa, not less | 55,0 |
|
Total shrinkage, %, not more |
12,0 |
|
Water absorption (1320оС),%, not more |
1,0 |
|
Recommended firing temperature, оС |
1290-1320 |
FET-2P
Ceramic material ECOBODY FET-2P, technical requirements TU U 14.2-32359731- 001:2006 is a plastic product, designed for the production of electro-technical wares 110 subgroup (silicate porcelain) by means of plastic forming.
The product has stable quality, rather high strength in dry and fired state.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 67,0 | 21,5 | 0,55 | 0,55 | 0,4 | 0,22 | 2,6 | 0,9 | 5,6 |
Ceramic-Physical properties
| Moisture content, %, not more | 23,0 |
| Mesh residue 63 μm, %, not more | 4,0 |
| MoR, MPa, not less | 4,0 |
| Fired bending strength, MPa, not less | 55,0 |
| Total shrinkage, %, not more | 16,0 |
| Water absorption (1320оС),%, not more | 0,0 |
| Recommended firing temperature, оС | 1290-1320 |
FET-3P
Ceramic material ECOBODY FET-3P, technical requirements TU U 14.2-32359731- 001:2006 is a plastic product, designed for the production of electro-technical wares 130 subgroup (high-strength aluminous porcelain) by means of plastic forming.
The product has stable quality, rather high strength in dry and fired state.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 37,0 | 52,5 | 0,35 | 0,45 | 0,3 | 0,2 | 3,3 | 0,5 | 5,5 |
Ceramic-Physical properties
| Moisture content, %, not more | 24,0 |
| Mesh residue 63 μm, %, not more | 0,0 |
| Mesh residue 40 μm, %, not more | 0,50 |
| Fired bending strength, MPa, not less | 65,0 |
| Total shrinkage, %, not more | 18,0 |
| Water absorption (1360оС),%, not more | 0,0 |
| Recommended firing temperature, оС | 1330-1360 |
FET-3I
Ceramic material ECOBODY FET-3I, technical requirements TU U 14.2-32359731- 001:2006 is a powder-like product, designed for the production of electro-technical wares 130 sub-group (high-strength aluminous porcelain) according to technical requirements by means of isostatic pressing.
The product has stable quality, rather high strength in dry and fired state.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | LOI |
| 37,0 | 52,5 | 0,35 | 0,45 | 0,3 | 0,2 | 3,3 | 0,5 | 5,5 |
Ceramic-Physical properties
| Moisture content, %, not more | 3,0 |
| Mesh residue 63 μm, %, not more | 0,0 |
| Mesh residue 40 μm, %, not more | 0,50 |
| Fired bending strength, MPa, not less | 65,0 |
| Total shrinkage, %, not more | 14,0 |
| Water absorption (1360оС),%, not more | 0,0 |
| Recommended firing temperature, оС | 1330-1360 |