ChM-2P

Ceramic material ECOBODY ChM-2P, technical requirements TU U 14.2-32359731-001:2006 is a mix of chamotte powder with fine-milled fire-clays and fluxes. It is designed for the production of decorative-artistic wares with increased demand to strength and frost-resistance. It is ideal for landscape ceramics.

The product has stable quality, rather high strength in dry state, good forming properties. It is less sensitive to the drying process.

The material can be fired both in gas and in electric kilns.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
58,5 30,5 1,2 1,2 0,4 0,5 1,4 1,2 3,8

Ceramic-Physical properties

Moisture content, %, not more
Plastic body
20,0
Mesh residue 63 µm, %, not more 50
Available dispersity of chamotte powder, mm 0-0,5
0-1,0
0-2,0
Total shrinkage, %, not more 11,0
Water absorption (1250oC), %, not more 5,0
Recommended firing temperature, oC
1200-1250

ChM-3P

Ceramic material ECOBODY ChM-3P, technical requirements TU U 14.2-32359731-001:2006 is a mix of chamotte powder with fine-milled fire-clays and kaolin. It is designed for the production of decorative-artistic wares both for interior and exterior application (facade and landscape ceramics).

The product has stable quality, rather high strength in dry state, good forming properties. It is less sensitive to the drying process.

The material can be fired both in gas and in electric kilns.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
54,1 33,0 0,95 1,05 0,4 0,42 1,0 1,1 6,5

Ceramic-Physical properties

Moisture content, %, not more
Plastic body
21,0
Mesh residue 63 µm, %, not more 35
Available dispersity of chamotte powder, mm 0-0,5
0-1,0
0-2,0
Total shrinkage, %, not more 13,0
Water absorption (1280oC), %, not more 3,0
Recommended firing temperature, oC 1260-1280
Colour after firing (temperature 1280oC, full vitrification): grayish-white

ChM-4P

Ceramic material ECOBODY ChM-4P, technical requirements TU U 14.2-32359731-001:2006 is a mix of chamotte powder with fine-milled fire-clays, mineralizers and feldspar. It is designed for the production of decorative-artistic wares both for interior and exterior application (facade and landscape ceramics).

The product has stable quality, rather high strength in dry state, good forming properties. It is less sensitive to the drying process.

The material can be fired both in gas and in electric kilns.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
62,0 24,0 1,1 1,2 2,0 0,5 1,6 0,8 6,0

Ceramic-Physical properties

Moisture content, %, not more
Plastic body
20,5
Mesh residue 63 µm, %, not more 25,0
Available dispersity of chamotte powder, mm 0-0,5
0-1,0
0-2,0
Total shrinkage, %, not more 12
Water absorption (1200oC), %, not more 1,0
Recommended firing temperature, oC 1150-1200
Colour after firing (temperature 1200oC, full vitrification): beige

ChM-6P

Ceramic material ECOBODY ChM-6P, technical requirements TU U 14.2-32359731-001:2006 is a mix of fine-dispersed chamotte powder with fine-milled fire-clays and fluxes. It is designed for the production of light-firing wares of decorative-artistic purposes both for interior and exterior application (landscape ceramics, elements of the fronts and buildings).

The product is supplied as a plastic vacuum-processed ceramic body shaped like bars (brick-formed).

The product has stable quality, good forming properties. It is low-sensitive to the drying process.

The material can be fired both in gas and in electric kilns.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
60,0 28,5 0,85 1,0 0,52 0,45 2,1 1,7 4,5

Ceramic-Physical properties

Moisture content, %, not more
Plastic body
20,0
Mesh residue 63 µm, %, not more 30
Available dispersity of chamotte powder, mm 0-0,5
0-1,0
Total shrinkage, %, not more 12
Water absorption (1200oC), %, not more 3,5
Recommended firing temperature, оС 1150-1200
Colour after firing (1200оС): Cream-coloured

ChM-4F

Ceramic material ECOBODY ChM-4F, technical requirements TU U 14.2-32359731-001:2006 is a powdery product, produced on basis of fine-milled fire-clays, with high plasticity, high strength in dry state and stable quality.

The product is most suitable for the production of the engobes, building and decorative mixtures, as well as a correcting additive to ceramic materials of various compositions to improve their physicochemical and technological properties.

Chemical content, % (for dry material, average)
SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O LOI
60 26 1,0 1,5 0,4 0,6 2,4 0,5 7,5

Ceramic-Physical properties

Moisture content, %, not more 4,0
Mesh residue 63 µm, %, not more 5,0
Total shrinkage, %, not more 10,0
MoR 110oC, MPa, not less 9,5
Water absorption (1230oC), %, not more 2,0
Recommended firing temperature, oC 1200-1230
Colour after firing (1230oС, full vitrification)
L (lightness)
*b (+red/-green)
*a (+yellow/-blue)

78,0
2,4
15,0

The technical data presented here are indicative only. All sales are undertaken in accordance with “Donbas Ceramic Bodies” LLC conditions of sales.

The present product is produced in the supervised conditions determined by the Management Quality System which function in accordance with ISO 9001:2015 demands and has BV Certification. Number of Certificate: UA228088